 Solution

Irradiation both creates dislocation loops and supplies mobile point defects that allow existing dislocations to climb, rearrange and annihilate. At low initial dislocation density, net production can dominate; at high initial density, sink absorption and recovery can dominate. A simple illustrative rate equation isThus both initial states approach ${\rho }_{\mathrm{ss}}=A/B$ in this fixed-condition model. Here $D$ is irradiation dose, not a diffusion coefficient. The asymptote reflects a dynamic balance, not the cessation of damage. It need not be the same for different alloys, temperatures, dose rates or applied stresses.