The historical names identify potassium chlorate, ammonium nitrate and calcium carbonate. Their expected net thermal decomposition chemical equations, written in modern formulae, areandThe first gives potassium chloride and oxygen. A potassium perchlorate intermediate can occur during uncatalysed heating; the first chemical equation gives the final overall balance. The second represents the familiar nitrous oxide pathway, with hot water initially as vapour. It does not mean that ammonium nitrate has only one decomposition pathway: conditions, impurities and confinement can produce different gases and violent decomposition.^[ref]

The third is calcination of limestone to quicklime. Its extent depends on temperature and the partial pressure of carbon dioxide; removing carbon dioxide favours further decomposition. Reversing the process gives carbonation of calcium oxide.

For dissolution in hydrochloric acid, the corresponding balances areand“Magnesia” here means magnesium oxide, and “alumina” means aluminium oxide. Zinc undergoes an oxidation-reduction reaction, reducing hydrogen ions to molecular hydrogen. The oxides instead undergo acid-base reactions: hydrogen ions convert oxide into water, without hydrogen evolution. The chlorides are dissolved species in water, rather than anhydrous molecular salts necessarily existing intact in the solution. Strongly ignited aluminium oxide may dissolve slowly; the balance does not determine the rate.

Disperse a very small amount of the dry powder in a clean volatile solvent compatible with aluminium oxide, use brief gentle sonication to separate loose agglomerates, and place a dilute drop on a holey carbon-coated transmission electron microscopy grid. Wick away excess liquid and dry thoroughly. Look first at low magnification and select isolated particles or thin edges over holes, rather than an electron-opaque pile. Record a solvent-only grid to identify contamination and compare several independently prepared areas.

This is quick and preserves individual particles without mechanical thinning. However, spray pyrolysis can make hollow or porous particles that may fracture during sonication; sedimentation and drying can select sizes and aggregate particles. aluminium oxide is insulating, so charging or beam-induced changes can complicate images, and the carbon support can overlap weak contrast. Vary dose and dwell time to test stability. A projected image of one selected thin particle is not an unbiased three-dimensional size or porosity distribution of the whole powder.