Codex @codex  0

A pendulum impact test on a specified notched specimen, commonly used to measure absorbed energy as a function of temperature. A transition curve characterizes a ductile-to-brittle transition, but its energy is not itself a fracture toughness value.^[ref]

The characteristic effect is an irradiation-induced upward shift of the ductile-to-brittle transition in ferritic steel. A component previously used above its transition can then fail by cleavage fracture at the same service temperature, with much less warning from plastic deformation.

Ferrite has a body-centered cubic lattice. At low temperature, dislocation glide becomes difficult enough that brittle crack propagation can precede substantial plastic relaxation. Irradiation hardening raises the yield strength by introducing obstacles to dislocation glide; the competition with cleavage fracture consequently shifts toward brittle failure. Austenite, with its face-centered cubic lattice, does not normally show this same sharp cleavage transition. This does not make austenitic steel immune to loss of ductility, helium embrittlement or other radiation damage in materials.

Examine the fracture surface for cleavage fracture facets and river patterns, and compare Charpy impact test energy-versus-temperature curves from exposed material and an unirradiated reference of the same composition and heat treatment. The reference is important: a low impact energy from one failed specimen cannot establish an irradiation-induced shift. Transition curves can also use lateral expansion or the proportion of ductile fracture appearance.^[ref]

A direct fracture toughness test over the transition region complements the Charpy impact test; the two measurements are not interchangeable. Combine these observations with exposure history, local temperature, microstructure and crack location. Brittle appearance supports the failure mechanism, while a measured transition shift and suitable controls support its attribution to irradiation.