A researcher who coauthored atomic-scale studies of metallic nanoparticles using scanning transmission electron microscopy. An aberration-corrected instrument combined images of atomic columns with chemical analysis to investigate gold particles and particles containing two metals. This combination helps distinguish changes in shape from changes in composition, which can look deceptively similar in a single projection.^[ref]

For cubic lattice planes, $d_{hkl}=a/\sqrt{h^2+k^2+l^2}$. The face-centred cubic selection rule permits indices that are all odd or all even. ThusThe first two spacings exceed the quoted 0.19 nm real-space resolution, whereas $d_{220}$ does not. This restriction is for the resolved image and its transform; a diffraction instrument need not have the same cutoff.

A natural candidate is a beam near a local $⟨110⟩$ zone axis. For example, the $[110]$ zone law $h+k=0$ includes four $\{111\}$ reflections and two $\{200\}$ reflections, all within that real-space cutoff. Their reciprocal-space length ratio is $g_{200}/g_{111}=2/\sqrt{3}=1.1547$. The angle between $(1\bar{1}1)$ and $(1\bar{1}\bar{1})$ reciprocal vectors is ${\cos }^{-1}(1/3)=70.53^{\circ }$. In contrast, a $[001]$ view gives a fourfold arrangement of the resolvable $\{200\}$ family, while the lowest ordinary $[111]$ zone reflections are $\{220\}$ and would not be resolved at the stated cutoff.

In a five-domain decahedral interpretation, neighboring tetrahedral fcc regions meet on $\{111\}$ twin planes around a common near-$⟨110⟩$ axis. Five unstrained wedges supply $5\times 70.53^{\circ }=352.64^{\circ }$; elastic distortion accommodates the remaining $7.36^{\circ }$. Their rotated diffraction contributions need not resemble a single six-spot $[110]$ pattern. Near-$⟨110⟩$ fcc domains in a multiply twinned particle are a defensible orientation proposal, not a unique full indexing. The printed transform has no reciprocal-space scale or indexed spot list, so it cannot establish every domain rotation or exclude an overlapping-particle contribution. Calibrated spacings and transforms from individual regions would settle those distinctions. The five-domain geometry is independently observed in atomic-resolution gold-particle measurements.^[ref]