Loss of resistance to cracking associated with hydrogen in a material. Mechanisms are material-dependent; brittle hydride precipitation is particularly relevant to zirconium alloys.

Nuclear fuel cladding has to retain the nuclear fuel and its fission products, transfer heat to the coolant, and preserve a usable mechanical geometry throughout irradiation. Those functions impose several coupled requirements.

Its neutron absorption cross section should be small: absorption in a structural tube removes neutrons without producing useful fuel fission. This is a major attraction of zirconium alloys in a thermal-spectrum nuclear reactor. Low absorption alone is insufficient, because the material must also tolerate its coolant and irradiation environment.

The tube needs adequate yield strength, fracture toughness and ductility to withstand pressure differences, handling, thermal cycling and fuel expansion. Resistance to material creep and mechanical fatigue limits progressive deformation and cracking. The design must accommodate changes in pressure and contact with the expanding fuel, including pellet-cladding mechanical interaction.

The coolant-facing surface should resist corrosion and loss of protective oxide integrity. Hydrogen uptake and hydrogen embrittlement matter for zirconium alloys; chemical compatibility with the fuel and released fission products matters on the inner surface. Resistance to stress corrosion cracking is particularly important when chemical attack and tensile loading act together.

The material should transfer heat without an excessive temperature drop, retain mechanical integrity at the relevant temperatures, and remain dimensionally acceptable under radiation damage in materials. Irradiation growth, irradiation creep, void swelling and irradiation hardening can alter clearance, stresses and coolant passages even when the unirradiated tube meets its specification.

Finally, the alloy should be manufacturable as thin, reproducible, leak-tight tubing with reliable end joints and inspectable defects. Material selection balances these requirements: increasing strength by alloying, for example, can change corrosion, neutron absorption and irradiation behavior. A high melting point by itself does not establish suitability.

For zirconium alloys, the practical upper temperature is governed by time-dependent corrosion, material creep and loss of ductility, well before bulk melting. In ordinary water-reactor service, cladding surfaces are commonly in the several-hundred-degree range, with normal operation around the low-to-mid $300{}^{\circ }\mathrm{C}$ range in a pressurized water reactor. A quoted service limit must specify alloy, coolant chemistry, exposure time, stress and accumulated hydrogen; there is no universal temperature at which every zirconium tube abruptly fails.

Increasing temperature accelerates zirconium-steam oxidation and creep. Oxide growth increases thermal resistance, and hydrogen uptake can leave a hydride-containing cladding with reduced resistance to cracking. A transient can also cause ballooning or rupture as hot material loses strength under internal pressure. Oxygen absorbed beneath the oxide stabilizes a brittle oxygen-rich region; a tube that survives the hot part of a transient can still have poor ductility during cooling and quenching.

For scale, the established US emergency-core-cooling criterion discussed by the United States Nuclear Regulatory Commission fuel-damage criteria limits peak cladding temperature to $2200{}^{\circ }\mathrm{F}$, about $1204{}^{\circ }\mathrm{C}$, together with an oxidation criterion. This is an accident-analysis criterion, rather than a proposed continuous service temperature.^[ref]

These material constraints limit allowable fuel heat flux and temperature excursions and require adequate heat removal and thermal margin. A small increase in coolant temperature or oxide thermal resistance can raise the underlying metal temperature and accelerate degradation. Alloy changes, protective coatings and alternative claddings aim to improve that margin, while still satisfying the neutronic and mechanical requirements.

A hydrogen-containing zirconium phase that can precipitate from hydrogen-bearing zirconium alloys. Brittle hydride platelets and their orientation affect cracking resistance; their behavior differs from dissolved hydrogen.