Polyethylene terephthalate ($({\mathrm{C}}_{10}{\mathrm{H}}_8{\mathrm{O}}_4{)}_n$)

Polyethylene terephthalate, more explicitly poly(ethylene terephthalate), is a polyester made from ethylene-glycol and terephthalate-derived units. It is often called PET polymer in materials contexts. Its chain contains repeated ester connections and para-substituted aromatic rings; it is not polyethylene with a physically mixed additive. ACS identifies the material as a condensation polymer of ethylene glycol and terephthalic acid.^[ref]

An ideal repeat can be writtenwith the two aromatic attachments opposite one another. Counting this repeat gives ${\mathrm{C}}_{10}{\mathrm{H}}_8{\mathrm{O}}_4$. The same count follows from the monomer formulas:This is repeat-unit bookkeeping; exact finite-chain composition also includes the end groups.

Using standard rounded atomic masses, the repeat contributes about $192.17\mathrm{g}\mathrm{mo}{\mathrm{l}}^{-1}$. An original ideal chain with 1000 such repeats therefore has about $192.17\mathrm{kg}\mathrm{mo}{\mathrm{l}}^{-1}$ of repeat-unit mass before end-group corrections. A real sample has a molar mass distribution; the repeat count does not assign one molecular mass to every chain.

The ester connections are part of the polymer backbone. Their cleavage by hydrolysis can shorten chains before all products leave the specimen, so retained mass and number-average molar mass need separate observations. Polymer fraction-recovery balance is relevant when soluble fragments and retained material are sampled differently. Neither the polyester label nor a bottle's disappearance from view identifies a degradation mechanism.

An illustrative comparison takes two samples with identical repeat chemistry but different crystallization and processing histories. Their thermal and mechanical responses can differ without a change in the repeat formula. A proposed experiment compares thermal response and chain-distribution measurements under documented conditioning, while checking for hydrolytic change during preparation. This separates molecular identity, chain length and material organization. The derivations here describe an ideal structure; no universal processing temperature or degradation rate is inferred from it.