In 1986, Johannes Georg Bednorz and Karl Alexander Müller precipitated mixed oxalates from aqueous barium, lanthanum and copper nitrates using oxalic acid. Heating at $900{}^{\circ }\mathrm{C}$ for five hours preceded pressing at $4\mathrm{kbar}$ and reheating for sintering. X-ray diffraction resolved three phases. Rectangular pieces carried gold electrodes and indium wires; four-terminal sensing in a continuous-flow cryostat measured electrical resistance versus temperature. Annealing atmosphere and measuring electric current density were varied; larger electric current densities suppressed the drop. An onset near $35\mathrm{K}$ differed from the much lower temperature where the drop approached three orders of magnitude.^[ref]

This was evidence for possible granular superconductivity, with phase identification unfinished. The paper deferred Meissner effect and heat capacity tests; its proof note corrected bulk lanthanum/barium ratios. A resistive onset did not establish a uniform bulk superconducting transition temperature.^[ref]

Their 1987 authored lecture describes later magnetometer checks on lead, followed by magnetic susceptibility measurements: samples with a resistive drop developed diamagnetism at somewhat lower temperatures. Combining magnetic, transport and X-ray diffraction results identified barium-substituted $\mathrm{L}{\mathrm{a}}_2\mathrm{Cu}{\mathrm{O}}_4$ as the superconducting phase. These later results strengthened the case beyond the initial mixed-phase transport evidence.^[ref]

Georg Bednorz and K. Alex Müller investigated oxide compositions that displayed a striking electrical resistivity decrease on cooling. Their 1986 report described oxygen-deficient barium-lanthanum-copper compounds, with a superconducting-like onset in the 30 kelvin range. Because the samples contained several phases, a connected conducting path could dominate electrical resistance before the whole specimen behaved uniformly. The work connected materials chemistry and electrical measurements in the emergence of high-temperature superconductivity.^[ref]

A solid-state physicist who researched metallic oxides at IBM's Zurich laboratory.^[ref]

K. Alex Müller and Georg Bednorz found evidence for superconductivity in copper-oxide compounds at unexpectedly high temperatures. Their 1986 barium-lanthanum-copper-oxygen samples contained multiple phases and showed a large electrical resistivity drop with onset in the 30 kelvin range. The strong dependence on applied current and sample connectivity required cautious interpretation. This initial result redirected the search for high-temperature superconductors toward chemically complex oxides.^[ref]

A solid-state physicist who carried out physics research at IBM.^[ref]