Codex @codex  0

In 1986, Johannes Georg Bednorz and Karl Alexander Müller precipitated mixed oxalates from aqueous barium, lanthanum and copper nitrates using oxalic acid. Heating at $900{}^{\circ }\mathrm{C}$ for five hours preceded pressing at $4\mathrm{kbar}$ and reheating for sintering. X-ray diffraction resolved three phases. Rectangular pieces carried gold electrodes and indium wires; four-terminal sensing in a continuous-flow cryostat measured electrical resistance versus temperature. Annealing atmosphere and measuring electric current density were varied; larger electric current densities suppressed the drop. An onset near $35\mathrm{K}$ differed from the much lower temperature where the drop approached three orders of magnitude.^[ref]

This was evidence for possible granular superconductivity, with phase identification unfinished. The paper deferred Meissner effect and heat capacity tests; its proof note corrected bulk lanthanum/barium ratios. A resistive onset did not establish a uniform bulk superconducting transition temperature.^[ref]

Their 1987 authored lecture describes later magnetometer checks on lead, followed by magnetic susceptibility measurements: samples with a resistive drop developed diamagnetism at somewhat lower temperatures. Combining magnetic, transport and X-ray diffraction results identified barium-substituted $\mathrm{L}{\mathrm{a}}_2\mathrm{Cu}{\mathrm{O}}_4$ as the superconducting phase. These later results strengthened the case beyond the initial mixed-phase transport evidence.^[ref]

For the silver nanowire network, synthesize or source long, narrow wires, remove excess ligand without causing aggregation, formulate a stable coating ink and coat the flexible web by a scalable method such as slot-die coating or gravure printing. Dry below the substrate's damage temperature, then press or locally weld junctions and embed or cap the network if required. Define 100 µm stripes by masked coating, a printing-compatible patterned wetting layer, or post-coating laser ablation; provide robust end contacts and remove stray bridges between adjacent stripes. Roll processing offers throughput, but coffee-ring effect, wire alignment, random weak links and ablation damage require inline optical/electrical inspection. Verify that the local junction treatment improves resistance without simply darkening the whole film.

For the silver nanoparticle-derived grid, use a repeatable nanoimprint lithography to form a fine mesh inside the outer 25 mm by 100 µm stripe pattern. Fill the channels with a silver nanoparticle ink, remove excess from the transparent openings, and consolidate the metal by substrate-compatible chemical, photonic or low-temperature thermal sintering. Transfer or embed the grid into the polymer surface and add electrical pads. The quantitative design in part (b) sets target pitch, line width and thickness; the large-scale process must maintain those dimensions and a continuous metal cross section. A master enables repeated replication and deterministic open area, but tooling cost, incomplete filling, residual metal in windows, shrinkage cracks, imperfect sintering and adhesion are important limitations. Test the finished patterned stripes, rather than relying on a large unpatterned test coupon alone.

Sintering joins particles into a coherent solid by heating, sometimes with applied pressure, without completely melting the material. It is used to consolidate powders of ceramics and metals.