Past exam of the physics A course of the University of Cambridge / 2019 / Paper 2 / Section C / C10

A Bravais lattice is the set of positions generated by integer combinations of independent primitive translation vectors, $\mathbf{R}=n_1{\mathbf{a}}_1+n_2{\mathbf{a}}_2+n_3{\mathbf{a}}_3$. Every lattice point has the same translational environment. A crystal may additionally have a basis of several atoms attached to each lattice point; those atoms are not automatically separate points of its Bravais lattice.

A unit cell is a region whose translated copies fill the crystal without gaps or overlaps. It can be chosen for convenient symmetry, and a conventional cell may contain several lattice points. A primitive unit cell is a smallest such repeating cell, containing exactly one lattice point when boundary sharing is counted. Its shape is not unique, but its volume $\Omega =|{\mathbf{a}}_1\cdot ({\mathbf{a}}_2\times {\mathbf{a}}_3)|$ is fixed for a given lattice. For a monatomic Bravais crystal, each primitive cell contains one atom.

Interpret the sphere as an atom of iron, and assume neighbouring atoms touch without overlap. Its radius is $r=0.124\mathrm{nm}=1.24\times 10^{-10}\mathrm{m}$, and its mass is $m_{\mathrm{Fe}}=56u\simeq 9.30\times 10^{-26}\mathrm{kg}$, using atomic mass unit $u=1.66054\times 10^{-27}\mathrm{kg}$.

In the face-centered cubic lattice, atoms touch along a face diagonal: $\sqrt{2}{a}_F=4r$, so $a_F=2\sqrt{2}r=0.3507\mathrm{nm}$. Four atoms occupy a conventional cube. The hard-sphere atomic volume in cubic lattices therefore givesIn the body-centered cubic lattice, atoms touch along the body diagonal: $\sqrt{3}{a}_B=4r$, so $a_B=4r/\sqrt{3}=0.2864\mathrm{nm}$. There are two atoms per conventional cube, givingThese are primitive unit cell volumes, not the volumes of the conventional cubes or of the atomic spheres. The denser FCC contact packing gives the higher mass density in this fixed-radius model. Actual hot phases have temperature-dependent dimensions and bonding, so these numbers should not be treated as exact experimental phase densities.

The reciprocal lattice is the set of wavevectors $\mathbf{G}$ satisfying $e^{i\mathbf{G}\cdot \mathbf{R}}=1$ for every direct Bravais lattice translation $\mathbf{R}$. Equivalently, $\mathbf{G}\cdot \mathbf{R}$ is an integer multiple of $2\pi$. It describes the spatial periodicities that can produce coherent Bragg scattering.

For direct primitive vectors ${\mathbf{a}}_i$ and oriented cell volume $\Omega ={\mathbf{a}}_1\cdot ({\mathbf{a}}_2\times {\mathbf{a}}_3)$, the primitive reciprocal vectors areThey obey ${\mathbf{a}}_i\cdot {\mathbf{b}}_j=2\pi {\delta }_{ij}$, and every reciprocal vector is an integer combination of them. Their units are inverse length. The reciprocal primitive cell volume is $(2\pi {)}^3/|\Omega |$, so expanding a direct lattice contracts its reciprocal scale.

The direct body-centered cubic lattice has a face-centred cubic reciprocal lattice, whereas the direct face-centered cubic lattice has a body-centred cubic reciprocal lattice. Thus the reciprocal lattice change in a structural phase transition reverses the two cubic types: the reciprocal lattice changes from FCC to BCC when the real material changes from BCC to FCC. If the direct conventional side is $a$, the reciprocal conventional side is $4\pi /a$ in either case, with the appropriate phase-specific $a$.

Within one phase, ordinary thermal expansion increases direct spacings and decreases reciprocal spacings. At the structural phase transition, reciprocal points acquire the new symmetry and allowed positions. A first-order transformation may show both phases simultaneously and may create differently oriented domains; it need not continuously preserve one perfect reciprocal array throughout.

Using the fixed-radius estimates from part (b), ${\Omega }_F/{\Omega }_B\simeq 0.919$, so the reciprocal primitive cell volume would increase by about $8.9\%$. That comparison belongs to the ideal contact model. The question supplies neither the actual thermal expansion nor a crystallographic orientation relationship, so it does not determine a unique trajectory of individual reciprocal points during the transition.

Use temperature-dependent X-ray diffraction, with the crystal in a controlled heating stage and a detector measuring diffracted directions. A reflection occurs when the scattering wavevector matches a reciprocal lattice vector, or equivalently when Bragg's law $2d_{hkl}\sin \theta =\lambda$ is satisfied. Record peak positions and intensities while heating to infer changes in lattice spacings and structure.

A monatomic conventional BCC cell has nonzero crystal basis structure factor only when $h+k+l$ is even. For FCC the indices must be all even or all odd. The change in reflection selection and peak positions therefore distinguishes the phases. For instance, BCC starts with a $(110)$ family whereas FCC starts with $(111)$, when indexed in their own conventional cells.

The transformation can create multiple orientation variants, grains, strain and phase coexistence. A reciprocal point that formerly satisfied the diffraction geometry may disappear or move off a fixed detector; a loss of one spot alone does not identify the new phase. Thermal expansion shifts peaks, thermal motion weakens coherent intensities, and hot iron may oxidize without a protective atmosphere.

After transformation, scan crystal angle and scattering angle or use an area detector to locate the new reflections. If single-crystal order has been lost, powder X-ray diffraction or a sufficiently broad orientation survey collects rings or many grain reflections instead of relying on the original alignment. Index several new peaks using the FCC selection rule and fit their common lattice parameter; this probes the new structure even when the original crystal orientation is no longer usable.