Past exam of the soft condensed matter course of the University of Cambridge / 2019 / Section B / B5

Solvent quality. The Flory interaction parameter $\chi$ measures the free-energy cost of polymer–solvent contacts relative to like contacts. In the simplest lattice model,where $z_c$ is the coordination number and the $ϵ$ values are contact energies. For lattice-site volume $v_0$, the effective two-segment excluded volume is $v_{\mathrm{eff}}=v_0(1-2\chi )$. Its sign determines the leading tendency of a long dilute flexible chain.

For $\chi <1/2$, $v_{\mathrm{eff}}>0$: a good solvent favors a swollen coil because segment encounters are effectively repulsive. For $\chi =1/2$, the leading attraction and repulsion cancel, giving approximately ideal chain statistics. For $\chi >1/2$, effective attraction favors contraction in a poor solvent, eventually producing a compact polymer globule under sufficiently poor conditions. This does not mean that every finite-chain solution with $\chi >1/2$ is automatically phase-separated; that also depends on composition and chain length.

The condition $\chi =1/2$ is the theta temperature condition for that polymer–solvent pair. For an energetic model $\chi =A/T$, it occurs at $T=\Theta =2A$. More generally, if $\chi =A/T+B$, it occurs when $A/\Theta +B=1/2$. It is not the absence of all intermolecular interactions and does not require the polymer and solvent to be chemically identical.

Chain dimensions. Interpret $R$ as the root-mean-square end-to-end distance of a polymer chain. Let $a$ denote the supplied statistical step length, calibrated to the same count $N$ as the degree of polymerization. At the theta condition, random-walk statistics giveFor a good solvent, the Flory approximation balances entropic stretching and two-segment interaction:Minimization gives $R^5\sim v_{\mathrm{eff}}{a}^2{N}^3$, henceThus the familiar good-solvent scaling is $R\sim a{N}^{3/5}$ when its nonuniversal solvent-quality amplitude is suppressed. With the additional lattice estimate $v_0\simeq a^3$, the more explicit form is $R\sim a(1-2\chi {)}^{1/5}{N}^{3/5}$. This swollen-coil estimate is used away from the narrow theta crossover; it must not be extrapolated to predict $R=0$ as $\chi \uparrow 1/2$. The crossover occurs when $(1-2\chi )N^{1/2}$ is of order one. Nearer theta, the ideal-coil size supplies the appropriate limit.

Numerical sizes. The theta value isFor $\chi =0.3$, the plain good-solvent scaling givesIf the solvent-quality amplitude is retained with $v_0=a^3$, it instead givesThe distinction is an explicitly stated modeling convention: the question does not give a microscopic site volume or an absolute swollen-coil prefactor. Both estimates describe a coil larger than the theta coil. Here $(1-2\chi )\sqrt{N}\simeq 15.5$, so a swollen-coil estimate is reasonable. Neither result is an exact microscopic prediction from the supplied data alone.

Overlap concentration. The polymer overlap concentration corresponds to one chain per coil volume. Using the scaling convention $V_{\mathrm{coil}}\sim R_{\theta }^3$ givesThe first is chain number density; the second counts repeat units. Thus the repeat-unit molar concentration is approximately $0.143\mathrm{mol}{\mathrm{L}}^{-1}$. If the lattice-site volume is taken as $v_0=a^3$, this is equivalentlyFor a mass-concentration estimate, a polystyrene repeat unit ${\mathrm{C}}_8{\mathrm{H}}_8$ has molar mass about $104.15\mathrm{g}\mathrm{mo}{\mathrm{l}}^{-1}$, so this scaling convention givesThere is no sharp coil surface fixing an exact numerical prefactor. For example, using the often adopted geometric definition $V_{\mathrm{coil}}=4\pi R_g^3/3$, with the ideal chain radius of gyration $R_g=R_{\theta }/\sqrt{6}=10.6\mathrm{nm}$, gives $c^{\ast }\simeq 52\mathrm{g}{\mathrm{L}}^{-1}$. The invariant content is one chain per coil volume and the theta scaling ${\varphi }^{\ast }\propto N^{-1/2}$; the radius and coil-volume convention must accompany a numerical value.

Osmotic pressure. In the given lattice expression, $\varphi$ is a dimensionless polymer volume fraction, not a dimensional number density, and $f$ is the mixing free energy per lattice site. Introduce $v_0$ to obtain a physical osmotic pressure. If $M=N_s+N{N}_p$ is the number of sites and $\varphi =N{N}_p/M$, differentiation of $F_{\mathrm{mix}}=Mf(\varphi )$ with respect to the solvent count at fixed chain count givesBalancing this change in solvent chemical potential against the pressure contribution $v_0\Pi$ gives $\Pi =(\varphi f^{\prime }-f)/v_0$. For composition-independent $\chi$,and therefore the osmotic pressure in Flory-Huggins solution theory isExpanding the logarithm as $\varphi \to 0$ givesThe first term is $n_p{k}_{B}T$ with $n_p=\varphi /(N{v}_0)$ now denoting chain number density: a whole chain supplies one translational contribution. The sign of the quadratic correction reproduces the solvent-quality classification. It is positive for a good solvent, zero at the theta temperature, and negative for a poor solvent. This is the same two-segment interaction that swells or contracts a single coil. At theta, a positive third-order contribution remains; the chain is approximately ideal in its large-scale conformation, not a gas of segments with no interactions at all.