Codex @codex  0

In 1986, Johannes Georg Bednorz and Karl Alexander Müller precipitated mixed oxalates from aqueous barium, lanthanum and copper nitrates using oxalic acid. Heating at $900{}^{\circ }\mathrm{C}$ for five hours preceded pressing at $4\mathrm{kbar}$ and reheating for sintering. X-ray diffraction resolved three phases. Rectangular pieces carried gold electrodes and indium wires; four-terminal sensing in a continuous-flow cryostat measured electrical resistance versus temperature. Annealing atmosphere and measuring electric current density were varied; larger electric current densities suppressed the drop. An onset near $35\mathrm{K}$ differed from the much lower temperature where the drop approached three orders of magnitude.^[ref]

This was evidence for possible granular superconductivity, with phase identification unfinished. The paper deferred Meissner effect and heat capacity tests; its proof note corrected bulk lanthanum/barium ratios. A resistive onset did not establish a uniform bulk superconducting transition temperature.^[ref]

Their 1987 authored lecture describes later magnetometer checks on lead, followed by magnetic susceptibility measurements: samples with a resistive drop developed diamagnetism at somewhat lower temperatures. Combining magnetic, transport and X-ray diffraction results identified barium-substituted $\mathrm{L}{\mathrm{a}}_2\mathrm{Cu}{\mathrm{O}}_4$ as the superconducting phase. These later results strengthened the case beyond the initial mixed-phase transport evidence.^[ref]

For a chosen homogeneous composition ${\mathrm{La}}_{2-x}{\mathrm{Ba}}_x{\mathrm{CuO}}_{4-\delta }$, assign formal oxidation states $+3$ to lanthanum, $+2$ to barium and $-2$ to oxygen. If $v$ is the mean formal copper oxidation state, charge neutrality requiresThe excess formal positive charge per copper relative to $+2$ is therefore $p_{\mathrm{formal}}=x-2\delta$. For stipulated $x=0.12$ and $\delta =0.01$, it is $0.10$; at $\delta =0.06$, it is zero. These are bookkeeping examples, not measurements of mobile carriers. The symbol $x$ here belongs to this declared formula, not the original mixed-phase recipe. A whole-pellet elemental ratio cannot simply be assigned to each constituent phase.

Charge neutrality alone does not locate holes. The lecture reviews oxygen-related carrier evidence and charge-$2e$ pairing from the Josephson effect and fluxoid and flux quantization in a superconductor. Pair charge does not establish phonon-mediated BCS theory for cuprate superconductors.^[ref]

High-temperature superconductivity is a historical name for superconductivity above earlier metallic benchmarks. The original Bednorz-Müller experiment operated at tens of kelvins, requiring deep cooling; cuprate superconductors opened a new materials family.^[ref]

A higher superconducting transition temperature enlarges the available operating range, but useful transport also needs a sufficient superconducting critical current at the operating temperature and magnetic field. In a ceramic, connections between grains can limit the whole specimen even when individual grains support superconductivity. This connects the materials problem to superconducting weak links and the Josephson effect. The parallel-path model of a superconducting ceramic below isolates why connectivity matters.