Codex @codex  0

Atomic force microscopy senses tip–sample interactions through a compliant cantilever. Contact deflection, oscillation amplitude, phase or resonance frequency can be converted into a feedback signal. Chemical bonding and short-range repulsion, van der Waals forces, electrostatic forces and, where relevant, magnetic or capillary interactions produce contrast. Apparent height at a fixed force or frequency setpoint can therefore contain interaction contrast as well as geometry. Lateral resolution depends on the effective tip apex and interaction range; finite tip radius broadens features. Vertical sensitivity also depends on thermal and detector noise, cantilever calibration, vibration, drift and feedback bandwidth. Strongly localized short-range forces favor atomic resolution, whereas extended interactions average over more of the tip and surface.

For small oscillations about equilibrium separation $z_0$, write $z=z_0+x$ and linearize $F(z)=F(z_0)+F^{\prime }(z_0)x$. The constant force is absorbed into the equilibrium displacement. The cantilever equation becomesConsequently the small-amplitude AFM frequency shift isThe linear expression is the small-force-gradient approximation, $|F^{\prime }|\ll c$, in addition to the small-oscillation assumption. For an attractive force $F=-C/z^2$, $F^{\prime }>0$ and the resonance softens. A finite oscillation amplitude samples a weighted range of forces rather than only the gradient at one separation, and $F^{\prime }\ge c$ destroys local stability in this simple static model.

In a scanning electron microscope, a focused electron beam scans the surface and a detector records an emitted signal at each beam position. Low-energy secondary electrons escape from near the surface; changes in local slope, edges and detector-facing geometry give strong secondary-electron topographic contrast. Backscattered electrons result from elastic deflection of primary electrons and generally have a larger yield for higher atomic number. Their backscattered-electron atomic-number contrast therefore helps separate compositional regions. Detector geometry, crystal orientation and topography can also affect this signal, so brightness is not a unique elemental identification.

An environmental scanning electron microscope admits gas around the specimen while pressure-limiting apertures and differential pumping preserve the electron-optical column's vacuum. Electron collisions ionize the gas. Positive ions can neutralize negative charging of a poorly conducting specimen, enabling observation without a conductive coating. A gaseous secondary electron detector uses gas amplification to collect secondary-electron signals under these conditions. Gas pressure, path length and scattering must be controlled because they also affect the probe and background.^[ref]

Finally, acquire an energy-dispersive X-ray spectroscopy spectrum at each pixel to add elemental specificity. The beam creates inner-shell vacancies, and characteristic X-rays emitted as they fill identify chemical elements. Selecting fitted characteristic-line intensities yields elemental maps that can be compared with the electron image. Peak overlap, detector response, absorption and the X-ray-generating interaction volume limit identification, quantification and spatial resolution. This gives chemical-element contrast; resolving different bonds or oxidation states generally needs more detailed spectral information than one broad elemental map.

SEM with energy-dispersive X-ray spectroscopy can identify gold versus silver through their characteristic X-ray energies. Acquire spectra and maps from representative regions: two compositionally distinct regions would support the two-phase interpretation of B. With standards or validated matrix corrections it can estimate local compositions and, with representative sampling, an overall composition. Surface topography and the interaction volume limit spatial interpretation.

X-ray fluorescence provides a complementary more bulk-averaged elemental measurement. Gold and silver produce different characteristic lines; calibrated intensities can yield their mass fractions, with corrections for absorption, excitation and specimen geometry. It does not by itself determine whether an element occupies one or two crystallographic phases.

Both methods supply elemental information missing from a lattice-parameter-only identification. A purely morphological micrograph could reveal phase separation but would not alone give a reliable numerical chemical composition.