Meaning of the mixing free energy. The supplied expression is the Flory–Huggins solution theory mixing free energy per lattice site, or per solvent-sized reference cell. Although the question calls it “per particle,” it cannot mean per polymer molecule: one chain occupies $N$ sites. Let the site volume be $v_0$, the total number of sites be $M=V/v_0$, and the chain and solvent counts be $n_p,n_s$, sowhereThe first term is the polymer's translational entropy of mixing. Its factor $1/N$ expresses that $N$ connected segments translate as one molecule. The second is the solvent's translational mixing entropy. Both are negative in the mixing free energy for $0<\varphi <1$, favoring mixing.

The final term is a mean-field excess contact contribution. The Flory interaction parameter $\chi$ measures the relative preference for unlike polymer-solvent contacts compared with like contacts. In the simplest lattice model with coordination number $z$ and pair energies ${ϵ}_{ps},{ϵ}_{pp},{ϵ}_{ss}$,Positive $\chi$ penalizes unlike contacts and promotes separation; negative $\chi$ favors them. Effective real-solution values can also include non-enthalpic effects, so their temperature dependence need not be exactly a constant divided by $T$. The subsequent derivatives assume composition-independent $\chi$ as in the supplied model.

Osmotic pressure and the special value one half. At fixed chain count, $\partial \varphi /\partial V=-\varphi /V$. Differentiating $F_{\mathrm{mix}}=(V/v_0)k_{B}Tg(\varphi )$ with respect to volume, relative to the pure-solvent reference, givesThe resulting osmotic pressure in Flory-Huggins solution theory isThe leading term is the ideal osmotic pressure of chains, since their number density is $\varphi /(N{v}_0)$. At $\chi =1/2$ the second-virial term vanishes: effective two-segment attraction and excluded-volume repulsion balance. This is the theta solvent condition for a sufficiently long dilute chain; the positive third-order contribution remains, so a finite-concentration solution is not a completely noninteracting gas. The site-volume factor is necessary to give physical pressure units.

For $\chi <1/2$, the effective pair excluded volume is positive. In a good solvent, the isolated chain expands relative to a Gaussian coil, with $R\sim b{N}^{\nu }$, $\nu \simeq 0.588$ or $3/5$ in the Flory approximation. For $\chi >1/2$, attraction wins in a poor solvent and a sufficiently long chain collapses toward a dense polymer globule, with asymptotic size $R\propto N^{1/3}$. Close to the theta condition, finite-chain crossover effects matter. At $\chi =1/2$, $R\sim b{N}^{1/2}$ to leading scaling order. This theta criterion is not the exact finite-$N$ phase-separation critical point; the lattice model has ${\varphi }_c=1/(1+\sqrt{N})$ and ${\chi }_c=(1+1/\sqrt{N}{)}^2/2$.

Overlap concentration. The polymer overlap concentration is reached when there is roughly one isolated coil in its own pervaded volume. If the coil size is $R$ and a repeat unit occupies volume $v_0$,With $R\sim b{N}^{\nu }$, the general scaling law isThe usual single-segment-volume estimate $v_0\sim b^3$ gives ${\varphi }^{\ast }\sim N^{1-3\nu }$: $N^{-1/2}$ in a theta solvent, approximately $N^{-4/5}$ in a good solvent, and order one for compact globules. A coil has no sharp surface, so choosing a radius of gyration or a geometric coil volume changes numerical prefactors.

For the stated polystyrene at $N=1500$ and $\chi =1/2$, the conventional scaling estimate isThis is a volume-fraction estimate, not a molar concentration. It uses the implicit site-volume approximation; the question does not provide an independent repeat-unit volume to determine a more precise prefactor.

Semidilute length scale. Beyond overlap, a semidilute polymer solution is characterized locally by a concentration blob size $\xi$. Suppose one blob contains $g$ statistical units. At the theta condition the subchain is Gaussian, so $\xi \sim b\sqrt{g}$, while matching its internal concentration to the bulk gives $\varphi \sim g{v}_0/{\xi }^3$. Eliminating $g$ gives the concentration-blob size in a theta solvent:Using the supplied statistical step length $b=0.67\mathrm{nm}$ and $\varphi =0.05$,The same convention gives $g\sim {\varphi }^{-2}=400<N=1500$, and the whole ideal chain has $R\sim b\sqrt{N}\simeq 26\mathrm{nm}$. Thus the blob is smaller than the chain. Because $\varphi /{\varphi }^{\ast }\simeq 1.94$ is only modestly above overlap, the value is a scaling estimate in a crossover region, not a precision asymptotic measurement. A statistical step length is not automatically a physical monomer diameter: if $v_0$ differs from $b^3$, the more general estimates are ${\varphi }^{\ast }\sim (v_0/b^3)N^{-1/2}$ and $\xi \sim v_0/(b^2\varphi )$, with the missing prefactor left explicit.