Past exam of the physics B course of the University of Cambridge / 2010 / Paper 1 / Section B / B9 / Solution

stress describes internal force per area. A cut with unit normal $\hat{\mathbf{n}}$ has traction $\mathbf{t}=\mathbf{\sigma }\hat{\mathbf{n}}$; its normal component is $\hat{\mathbf{n}}\cdot \mathbf{\sigma }\hat{\mathbf{n}}$ and its remainder is shear traction. force balance constrains the stress divergence, while ordinary local angular-momentum balance makes the Cauchy stress tensor symmetric in a medium without body couples.

strain describes deformation rather than force. For small displacement gradients,The antisymmetric displacement-gradient part is a rigid rotation to first order and contributes no infinitesimal strain. Engineering shear strain is ${\gamma }_{xy}=2{ϵ}_{xy}$, so it must not be confused with the tensor component. stress has units of pressure; strain is dimensionless.

An isotropic linear elastic solid obeysTwo independent moduli are required. The shear modulus $G$ and bulk modulus $K=\lambda +2G/3$ must be positive for stability. Young's modulus and Poisson ratio satisfyFor a tensile specimen with free side faces, ${\sigma }_{xx}=F/A$ gives ${ϵ}_{xx}={\sigma }_{xx}/E$ and ${ϵ}_{yy}={ϵ}_{zz}=-\nu {\sigma }_{xx}/E$. Pure shear gives $\tau =G\gamma$; hydrostatic loading gives $\Delta V/V=-p/K$. The incompressible limit has $\nu \to 1/2$ at finite shear stiffness, not vanishing shear resistance. Crystals can be anisotropic and need a fourth-rank elastic stiffness tensor instead of the isotropic two-constant law.

elastic deformation is recoverable on unloading; it need not remain linear at large strain. Beyond yield, irreversible rearrangements such as dislocation motion cause plastic strain, often followed by hardening. Ductile samples can neck before fracture; brittle failure has much less plastic deformation. Engineering stress uses initial area, while true stress uses the changing instantaneous area. A decreasing engineering stress during necking therefore need not mean that local true stress decreases. stress concentrations, flaws and loading geometry can determine failure before a uniform-material strength is reached. Viscoelastic materials also show rate dependence, creep and stress relaxation; their losses cannot be described by a static Hooke law alone.

A tensile test should measure force and gauge-length extension independently, correct machine compliance, align the grips, and control strain rate and temperature. Unloading distinguishes recoverable strain from a residual plastic extension. Separate shear or hydrostatic tests determine moduli that one axial measurement does not fix. Compression specimens need friction and buckling checks. Work per volume is $\int {\sigma }_{ij}d{ϵ}_{ij}$; the recoverable part is elastic energy, while a dissipative cycle produces a loss rather than creating energy. The original loading/unloading curve below is a chosen constitutive sketch, not measured material data.