Physical Review Letters 66, 719–722. The abstract identifies end-grafted polydimethylsiloxane on porous silicon dioxide and reports thickness proportional to $M\sigma$ in a poor solvent and $M{\sigma }^{1/3}$ in a good solvent. The chemical system in that abstract differs from the polystyrene wording of the 2016 exam; the scaling comparison is unaffected.

The Flory interaction parameter measures the excess free-energy cost of unlike contacts in Flory–Huggins solution theory. For a simple lattice of coordination number $z_c$ and contact energies ${ϵ}_{ps}$, ${ϵ}_{pp}$ and ${ϵ}_{ss}$,Real effective parameters may also contain entropic contributions and composition dependence. With site volume $v_0$ and composition-independent $\chi$, the effective two-segment excluded volume is $v_{\mathrm{eff}}=v_0(1-2\chi )$. Positive, zero and negative $v_{\mathrm{eff}}$ correspond respectively to a good solvent, the theta temperature condition and a poor solvent. In particular, $\chi =1/2$ means cancellation of leading repulsive and attractive contributions; it does not mean that every molecular interaction vanishes.

Flocculation indicates that the attraction/kinetic balance has changed: electrolyte may screen a double-layer barrier; pH may reduce surface charge; multivalent ions can promote aggregation; added polymer can bridge particles or cause depletion force; poor solvent conditions can collapse stabilizing layers. Rapid evaporation concentrates both particles and salts and can force contacts faster than they anneal. Aggregates then sediment much faster because their effective buoyant size has grown.

Check ionic strength, pH, surface charge and the particle size distribution before and during assembly. Dialyse or reduce salt where appropriate, restore surface charge, add a nonbridging steric stabilization with a compatible solvent, and slow the concentration step. Compare untreated and deliberately salt-screened controls. Restoring repulsion after irreversible aggregation may not redisperse the particles, so prevention is preferable to assuming all settled material can be recovered.

At the theta condition, effective excluded volume approximately cancel and a freely jointed ideal chain has $⟨R^2⟩=N{b}^2$. With the stipulated segment length $b=2a$,In a good solvent repulsive excluded volume swells the coil, giving $R\sim b{N}^{\nu }$ with $\nu \simeq 0.588$ in three dimensions, or the Flory approximation $\nu =3/5$. In a poor solvent effective segment attraction favours a compact globule, whose linear size scales as $b{N}^{1/3}$ at roughly fixed internal density. The latter are scaling laws with model-dependent prefactors. A real chemical monomer need not be a statistical Kuhn length; using $2a$ as the independent segment length is part of this question's idealized model.

With polymer degree $N_A$ and single-site solvent molecules, Flory–Huggins solution theory gives $f/(k_{B}T)=(\varphi /N_A)\ln \varphi +(1-\varphi )\ln (1-\varphi )+\chi \varphi (1-\varphi )$. Expanding the solvent entropy at low concentration gives the dilute-polymer free-energy expansionThe linear term sets a reference chemical potential. The quadratic term controls the leading effective two-segment excluded volume, $v_{\mathrm{eff}}=v_0(1-2\chi )$ for site volume $v_0$.

In a good solvent, $\chi <1/2$ and positive excluded volume swells a dilute chain: the Flory approximation gives $R\sim b{N}_A^{3/5}$ in three dimensions. In a poor solvent, $\chi >1/2$ favors segment contacts and a sufficiently long isolated chain forms a polymer globule, with compact scaling $R\sim b{N}_A^{1/3}$ up to density-dependent factors.

At the theta temperature, the leading two-segment interaction cancels, $\chi =1/2$ in this model, and the long-chain conformation is approximately an ideal chain, $R\sim b\sqrt{N_A}$. The positive cubic term remains. The critical point of a Flory–Huggins polymer solution at finite $N_A$ has ${\chi }_c=\frac{1}{2}(1+N_A^{-1/2}{)}^2$; its limiting value, rather than every finite-chain critical point, is the theta condition.

Use polymer volume fraction $\varphi$ and interaction parameter $\chi$, increasing toward poor-solvent conditions. The Flory–Huggins solution theory free energy per lattice site isThe common-tangent construction gives the binodal; $f^{\prime \prime }=0$ gives the spinodal, $2{\chi }_s=1/(N\varphi )+1/(1-\varphi )$. Its critical point is ${\varphi }_c=1/(1+\sqrt{N})$, ${\chi }_c=\frac{1}{2}(1+N^{-1/2}{)}^2$. Above the binodal in this $\chi$ plot, the solution separates into polymer-poor and polymer-rich phases; between binodal and spinodal it is metastable, while inside the spinodal a homogeneous state is unstable.

The line $\chi =1/2$ is the theta solvent condition for a long dilute chain. Below it is the good solvent side; above it is the poor solvent side. Poor solvent does not imply that every composition is already phase separated. Independently, a homogeneous solution is dilute for $\varphi \ll {\varphi }^{\ast }$, semidilute for $\varphi \gg {\varphi }^{\ast }$ below close packing, and concentrated as $\varphi$ approaches one.

In water, the strongly poor solvent favours a compact polymer globule. A site-volume estimate givesThe exact numerical conversion between globule radius and rms end-to-end distance depends on its density and shape; this calculation supplies the characteristic size scale.

Here $R$ denotes a typical chain size, such as an rms end-to-end distance of a polymer chain, rather than the mean end-to-end vector of an isotropic solution, which is zero. The Flory approximation gives $R\sim a{N}^{3/5}$ in a good solvent, an ideal chain has $R\sim a{N}^{1/2}$ in a theta solvent, and a compact polymer globule has size $R\sim a{N}^{1/3}$ in a strongly poor solvent. These are scaling estimates with order-one prefactors omitted, treating the stated $N$ as the segment count associated with the supplied statistical length.

The Flory interaction parameter measures the energetic preference for unlike rather than like contacts in Flory–Huggins solution theory. For polymer volume fraction $\varphi$ and $N$ lattice sites per chain, the dimensionless mixing Helmholtz free energy per site isThe logarithmic terms represent combinatorial entropy; polymer connectivity reduces the chain's translational mixing entropy by the factor $N$. In a simple contact model $\chi =z[{ϵ}_{ps}-({ϵ}_{pp}+{ϵ}_{ss})/2]/(k_{B}T)$, where $z$ is the coordination number. Positive $\chi$ penalizes polymer-solvent contacts. Increasing it can overcome mixing entropy and cause phase separation; a negative second derivative of the mixing free energy marks the spinodal region. For a long dilute chain, $\chi <1/2$ corresponds to a good solvent, $\chi =1/2$ to the idealized theta condition, and $\chi >1/2$ to a poor solvent. Real effective parameters can depend on temperature and concentration, rather than being universal chemical constants.

The three solvent conditions describe effective interactions between segments of a generic polymer. In a good solvent, solvent contacts favor a swollen, self-avoiding coil with positive excluded volume. At a theta solvent condition, leading pair repulsion and attraction cancel; the chain has approximately ideal random-walk statistics. In a poor solvent, effective attraction contracts the chain, eventually producing a dense polymer globule for a sufficiently long chain.

For $N$ statistical segments of length $a$, the radius of gyration has the scalingThe good-solvent power $3/5$ is the Flory approximation; the asymptotic three-dimensional exponent is closer to $0.588$. In the ideal freely jointed chain, the more precise result is $R_g^2\simeq N{a}^2/6$, whereas the end-to-end mean square is $N{a}^2$. Scaling notation suppresses those geometry-dependent factors. The globule power follows from a volume proportional to $N$, and presumes a dense collapsed state away from the theta crossover. The dilute condition excludes overlap with other chains; it does not eliminate contacts between distant segments of the same chain.

Use polymer volume fraction $\varphi$ horizontally and the Flory interaction parameter $\chi$ vertically. Lower $\chi$ gives better solvent quality. The simplest Flory–Huggins solution theory assigns the dimensionless mixing free energy per lattice siteThus $\chi <1/2$ gives positive excluded volume and a good-solvent coil, $\chi =1/2$ is the long-chain theta condition, and $\chi >1/2$ is the poor-solvent side. It is the net two-segment interaction that vanishes at theta, not every molecular force.

At fixed good-solvent quality, the polymer overlap volume fraction ${\varphi }^{\ast }\sim N{a}^3/R_g^3$ separates isolated coils from a semidilute polymer solution. Above overlap, many chains interpenetrate, but there is still solvent on the segment scale. As $\varphi$ approaches order unity the solution is concentrated; these concentration-regime boundaries are crossovers, not first-order phase transitions. The overlap fraction increases from order $N^{-4/5}$ in a strong good solvent toward order $N^{-1/2}$ at theta. The crossover can be expressed as ${\varphi }^{\ast }\sim N^{-4/5}(1-2\chi {)}^{-3/5}$ while $1-2\chi \gg N^{-1/2}$; it saturates at the theta scaling when that condition fails.

On the poor-solvent side there can instead be coexistence of polymer-poor and polymer-rich phases. The binodal follows a common tangent of $f$; the spinodal followsThe critical point of a Flory–Huggins polymer solution isFor finite $N$, ${\chi }_c$ lies above $1/2$. Therefore poor solvent does not automatically mean demixing at every concentration, and an overlap line must not be mistaken for a coexistence boundary. The original figure uses the stated ideal model for an illustrative chain length; it does not assert a measured phase boundary. A vertical temperature axis would additionally require a material-specific relation $\chi (T)$.

The coil-globule transition is the contraction of an isolated flexible polymer as solvent quality worsens. A swollen chain in a good solvent has size $R\sim a{N}^{3/5}$ in the Flory approximation. At the theta temperature the effective two-segment excluded volume vanishes and $R\sim a{N}^{1/2}$. A poor solvent favors a dense polymer globule, with $R\propto N^{1/3}$ at fixed internal density.

The competition is visible in the scaling free energyFor $v>0$, elastic cost balances two-segment repulsion to give the swollen-coil law. At $v=0$, three-segment repulsion stabilizes ideal-chain scaling; for $v<0$, attraction balanced by the positive three-segment term gives $R^3\sim uN/|v|$. The dense polymer globule also has an interfacial free energy. The scaling expression explains regimes, not all fluctuation corrections or a detailed finite-chain transition curve. A finite chain crosses over smoothly; the sharp theta-point limit refers to indefinitely long chains.

A dilute-solution light-scattering experiment can follow radius of gyration while changing temperature or solvent composition. Measure at several concentrations and extrapolate toward isolated chains; check molecular-weight distribution, reversibility and the absence of growing multi-chain aggregates. dynamic light scattering measures hydrodynamic size, which is related to but distinct from radius of gyration. A falling scattering-derived size accompanied by a rising aggregate population cannot by itself establish single-chain collapse. solvent quality controls conformation through the balance of segment interactions and conformational entropy.

Interpret the stated free energy as per lattice site of volume $v_0$. Flory–Huggins solution theory counts polymer chains, giving the entropy term $(\phi /N)\ln \phi$, and solvent molecules, giving $(1-\phi )\ln (1-\phi )$. The interaction term penalizes unlike contacts when $\chi >0$; a simple contact model has $\chi =z[{ϵ}_{ps}-({ϵ}_{pp}+{ϵ}_{ss})/2]/(k_{B}T)$. Connectivity reduces polymer translational entropy relative to independent monomers. This is an incompressible mean-field model with composition-independent $\chi$ for the calculations below.^[ref]

Expanding the dilute osmotic pressure identifies the effective second virial coefficient. A good solvent has $\chi <1/2$ and positive excluded volume, promoting swollen chains. A poor solvent has $\chi >1/2$, favouring contraction and potentially phase separation. The theta-solvent condition is $\chi =1/2$ in this long-chain mean-field description: the second virial term vanishes, but higher terms remain. For finite $N$, this condition is not the exact critical point, which instead has ${\chi }_c=(1+N^{-1/2}{)}^2/2$.

Let $g=f_{\mathrm{mix}}/(k_{B}T)$. The osmotic pressure in Flory-Huggins solution theory isThus $\Pi =(k_{B}T/v_0)[\phi /N+(1/2-\chi ){\phi }^2+{\phi }^3/3+\cdots ]$. For mass concentration $c={\rho }_p\phi$ and chain molar mass $M_n=N{\rho }_p{v}_0{N}_A$,osmometry uses a membrane permeable to solvent but retaining every polymer chain, at known uniform temperature. Extrapolate $\Pi /c$ to zero concentration to remove interactions; the intercept gives the number-average molar mass. Aggregation, leakage of small chains, ions with a Donnan contribution, or a poor-solvent two-phase sample invalidate the simple molecular-weight interpretation.

The measured ratios give an exactly linear reduced-pressure fit:The reduced osmotic-pressure intercept is $185\mathrm{Pa}{\mathrm{m}}^3\mathrm{k}{\mathrm{g}}^{-1}$. The data determine $M_n/T=0.04494\mathrm{kg}\mathrm{mo}{\mathrm{l}}^{-1}{\mathrm{K}}^{-1}$; the measurement temperature is needed to convert this into an absolute molar mass. For an explicitly assumed room temperature $T=300\mathrm{K}$, $M_n\simeq 13.5\mathrm{kg}\mathrm{mo}{\mathrm{l}}^{-1}=1.35\times 10^4\mathrm{g}\mathrm{mo}{\mathrm{l}}^{-1}$. The boxed expression is the general answer for an arbitrary experimental temperature.

For a long ideal chain of $N$ statistical segments of length $b$, $R_G^2=N{b}^2/6$. At fixed repeat chemistry and statistical segment length, molar mass is proportional to $N$. The molecular-weight scaling of an ideal-chain gyration radius thus givesThe supplied size and ideal statistics are used as stipulated; an independently tabulated coil size would not replace the given baseline.

solvent quality changes the balance of segment–segment and segment–solvent contacts. In a good solvent, excluded-volume repulsion swells a sufficiently long isolated chain, with $R_G\propto N^{\nu }$, $\nu \simeq 0.588$ in three dimensions; the Flory approximation gives $\nu =3/5$. At theta conditions the effective two-segment excluded volume vanishes and the ideal exponent $1/2$ is recovered for long chains. A poor solvent favors a compact polymer globule, whose large-chain size scales approximately as $N^{1/3}$ at fixed internal density. solvent and temperature can also change local persistence length and hence the prefactor. These different conformations need not have the same radius at the same molar mass.

Meaning of the mixing free energy. The supplied expression is the Flory–Huggins solution theory mixing free energy per lattice site, or per solvent-sized reference cell. Although the question calls it “per particle,” it cannot mean per polymer molecule: one chain occupies $N$ sites. Let the site volume be $v_0$, the total number of sites be $M=V/v_0$, and the chain and solvent counts be $n_p,n_s$, sowhereThe first term is the polymer's translational entropy of mixing. Its factor $1/N$ expresses that $N$ connected segments translate as one molecule. The second is the solvent's translational mixing entropy. Both are negative in the mixing free energy for $0<\varphi <1$, favoring mixing.

The final term is a mean-field excess contact contribution. The Flory interaction parameter $\chi$ measures the relative preference for unlike polymer-solvent contacts compared with like contacts. In the simplest lattice model with coordination number $z$ and pair energies ${ϵ}_{ps},{ϵ}_{pp},{ϵ}_{ss}$,Positive $\chi$ penalizes unlike contacts and promotes separation; negative $\chi$ favors them. Effective real-solution values can also include non-enthalpic effects, so their temperature dependence need not be exactly a constant divided by $T$. The subsequent derivatives assume composition-independent $\chi$ as in the supplied model.

Osmotic pressure and the special value one half. At fixed chain count, $\partial \varphi /\partial V=-\varphi /V$. Differentiating $F_{\mathrm{mix}}=(V/v_0)k_{B}Tg(\varphi )$ with respect to volume, relative to the pure-solvent reference, givesThe resulting osmotic pressure in Flory-Huggins solution theory isThe leading term is the ideal osmotic pressure of chains, since their number density is $\varphi /(N{v}_0)$. At $\chi =1/2$ the second-virial term vanishes: effective two-segment attraction and excluded-volume repulsion balance. This is the theta solvent condition for a sufficiently long dilute chain; the positive third-order contribution remains, so a finite-concentration solution is not a completely noninteracting gas. The site-volume factor is necessary to give physical pressure units.

For $\chi <1/2$, the effective pair excluded volume is positive. In a good solvent, the isolated chain expands relative to a Gaussian coil, with $R\sim b{N}^{\nu }$, $\nu \simeq 0.588$ or $3/5$ in the Flory approximation. For $\chi >1/2$, attraction wins in a poor solvent and a sufficiently long chain collapses toward a dense polymer globule, with asymptotic size $R\propto N^{1/3}$. Close to the theta condition, finite-chain crossover effects matter. At $\chi =1/2$, $R\sim b{N}^{1/2}$ to leading scaling order. This theta criterion is not the exact finite-$N$ phase-separation critical point; the lattice model has ${\varphi }_c=1/(1+\sqrt{N})$ and ${\chi }_c=(1+1/\sqrt{N}{)}^2/2$.

Overlap concentration. The polymer overlap concentration is reached when there is roughly one isolated coil in its own pervaded volume. If the coil size is $R$ and a repeat unit occupies volume $v_0$,With $R\sim b{N}^{\nu }$, the general scaling law isThe usual single-segment-volume estimate $v_0\sim b^3$ gives ${\varphi }^{\ast }\sim N^{1-3\nu }$: $N^{-1/2}$ in a theta solvent, approximately $N^{-4/5}$ in a good solvent, and order one for compact globules. A coil has no sharp surface, so choosing a radius of gyration or a geometric coil volume changes numerical prefactors.

For the stated polystyrene at $N=1500$ and $\chi =1/2$, the conventional scaling estimate isThis is a volume-fraction estimate, not a molar concentration. It uses the implicit site-volume approximation; the question does not provide an independent repeat-unit volume to determine a more precise prefactor.

Semidilute length scale. Beyond overlap, a semidilute polymer solution is characterized locally by a concentration blob size $\xi$. Suppose one blob contains $g$ statistical units. At the theta condition the subchain is Gaussian, so $\xi \sim b\sqrt{g}$, while matching its internal concentration to the bulk gives $\varphi \sim g{v}_0/{\xi }^3$. Eliminating $g$ gives the concentration-blob size in a theta solvent:Using the supplied statistical step length $b=0.67\mathrm{nm}$ and $\varphi =0.05$,The same convention gives $g\sim {\varphi }^{-2}=400<N=1500$, and the whole ideal chain has $R\sim b\sqrt{N}\simeq 26\mathrm{nm}$. Thus the blob is smaller than the chain. Because $\varphi /{\varphi }^{\ast }\simeq 1.94$ is only modestly above overlap, the value is a scaling estimate in a crossover region, not a precision asymptotic measurement. A statistical step length is not automatically a physical monomer diameter: if $v_0$ differs from $b^3$, the more general estimates are ${\varphi }^{\ast }\sim (v_0/b^3)N^{-1/2}$ and $\xi \sim v_0/(b^2\varphi )$, with the missing prefactor left explicit.

Solvent quality. The Flory interaction parameter $\chi$ measures the free-energy cost of polymer–solvent contacts relative to like contacts. In the simplest lattice model,where $z_c$ is the coordination number and the $ϵ$ values are contact energies. For lattice-site volume $v_0$, the effective two-segment excluded volume is $v_{\mathrm{eff}}=v_0(1-2\chi )$. Its sign determines the leading tendency of a long dilute flexible chain.

For $\chi <1/2$, $v_{\mathrm{eff}}>0$: a good solvent favors a swollen coil because segment encounters are effectively repulsive. For $\chi =1/2$, the leading attraction and repulsion cancel, giving approximately ideal chain statistics. For $\chi >1/2$, effective attraction favors contraction in a poor solvent, eventually producing a compact polymer globule under sufficiently poor conditions. This does not mean that every finite-chain solution with $\chi >1/2$ is automatically phase-separated; that also depends on composition and chain length.

The condition $\chi =1/2$ is the theta temperature condition for that polymer–solvent pair. For an energetic model $\chi =A/T$, it occurs at $T=\Theta =2A$. More generally, if $\chi =A/T+B$, it occurs when $A/\Theta +B=1/2$. It is not the absence of all intermolecular interactions and does not require the polymer and solvent to be chemically identical.

Chain dimensions. Interpret $R$ as the root-mean-square end-to-end distance of a polymer chain. Let $a$ denote the supplied statistical step length, calibrated to the same count $N$ as the degree of polymerization. At the theta condition, random-walk statistics giveFor a good solvent, the Flory approximation balances entropic stretching and two-segment interaction:Minimization gives $R^5\sim v_{\mathrm{eff}}{a}^2{N}^3$, henceThus the familiar good-solvent scaling is $R\sim a{N}^{3/5}$ when its nonuniversal solvent-quality amplitude is suppressed. With the additional lattice estimate $v_0\simeq a^3$, the more explicit form is $R\sim a(1-2\chi {)}^{1/5}{N}^{3/5}$. This swollen-coil estimate is used away from the narrow theta crossover; it must not be extrapolated to predict $R=0$ as $\chi \uparrow 1/2$. The crossover occurs when $(1-2\chi )N^{1/2}$ is of order one. Nearer theta, the ideal-coil size supplies the appropriate limit.

Numerical sizes. The theta value isFor $\chi =0.3$, the plain good-solvent scaling givesIf the solvent-quality amplitude is retained with $v_0=a^3$, it instead givesThe distinction is an explicitly stated modeling convention: the question does not give a microscopic site volume or an absolute swollen-coil prefactor. Both estimates describe a coil larger than the theta coil. Here $(1-2\chi )\sqrt{N}\simeq 15.5$, so a swollen-coil estimate is reasonable. Neither result is an exact microscopic prediction from the supplied data alone.

Overlap concentration. The polymer overlap concentration corresponds to one chain per coil volume. Using the scaling convention $V_{\mathrm{coil}}\sim R_{\theta }^3$ givesThe first is chain number density; the second counts repeat units. Thus the repeat-unit molar concentration is approximately $0.143\mathrm{mol}{\mathrm{L}}^{-1}$. If the lattice-site volume is taken as $v_0=a^3$, this is equivalentlyFor a mass-concentration estimate, a polystyrene repeat unit ${\mathrm{C}}_8{\mathrm{H}}_8$ has molar mass about $104.15\mathrm{g}\mathrm{mo}{\mathrm{l}}^{-1}$, so this scaling convention givesThere is no sharp coil surface fixing an exact numerical prefactor. For example, using the often adopted geometric definition $V_{\mathrm{coil}}=4\pi R_g^3/3$, with the ideal chain radius of gyration $R_g=R_{\theta }/\sqrt{6}=10.6\mathrm{nm}$, gives $c^{\ast }\simeq 52\mathrm{g}{\mathrm{L}}^{-1}$. The invariant content is one chain per coil volume and the theta scaling ${\varphi }^{\ast }\propto N^{-1/2}$; the radius and coil-volume convention must accompany a numerical value.

Osmotic pressure. In the given lattice expression, $\varphi$ is a dimensionless polymer volume fraction, not a dimensional number density, and $f$ is the mixing free energy per lattice site. Introduce $v_0$ to obtain a physical osmotic pressure. If $M=N_s+N{N}_p$ is the number of sites and $\varphi =N{N}_p/M$, differentiation of $F_{\mathrm{mix}}=Mf(\varphi )$ with respect to the solvent count at fixed chain count givesBalancing this change in solvent chemical potential against the pressure contribution $v_0\Pi$ gives $\Pi =(\varphi f^{\prime }-f)/v_0$. For composition-independent $\chi$,and therefore the osmotic pressure in Flory-Huggins solution theory isExpanding the logarithm as $\varphi \to 0$ givesThe first term is $n_p{k}_{B}T$ with $n_p=\varphi /(N{v}_0)$ now denoting chain number density: a whole chain supplies one translational contribution. The sign of the quadratic correction reproduces the solvent-quality classification. It is positive for a good solvent, zero at the theta temperature, and negative for a poor solvent. This is the same two-segment interaction that swells or contracts a single coil. At theta, a positive third-order contribution remains; the chain is approximately ideal in its large-scale conformation, not a gas of segments with no interactions at all.

For $N=300$, the critical polymer volume fraction isIf $v_0$ is the volume assigned to one amino acid in the lattice model, the critical number densities are exactlyThe extra physical approximation needed to use the given radius of gyration is that a chain in a poor solvent is a compact polymer globule. Its size then scales as $R_g\sim b{N}^{1/3}$ with $v_0\sim b^3$, so $N{v}_0\sim R_g^3$. This gives the standard scaling estimatesWith $R_g=3\mathrm{nm}$, numerical substitution givesUsing only the leading large-$N$ value ${\varphi }_c\sim N^{-1/2}$ gives $6.4\times 10^{26}$ and $2.1\times 10^{24}{\mathrm{m}}^{-3}$, respectively. These are scaling estimates, not geometrically exact densities.

For comparison, a specifically uniform spherical compact protein has the radius of gyration of a uniform sphere, $R_g^2=3R^2/5$, so its physical volume is $V_p=(4\pi /3)(5/3{)}^{3/2}{R}_g^3$. Taking $N{v}_0=V_p$ instead gives $n_{m,c}\simeq 6.7\times 10^{25}{\mathrm{m}}^{-3}$ and $n_{p,c}\simeq 2.2\times 10^{23}{\mathrm{m}}^{-3}$. The factor between these conventions is geometric. The PDF does not give a monomer volume, globule density or shape model, and a radius of gyration alone does not determine an exact molecular volume. The model-independent conclusions are the formulas in terms of $v_0$ and the 300:1 ratio of monomer to protein number density.

A polymer globule is a compact conformation favored by effective segment attractions in a poor solvent. If its internal segment density is independent of chain length, its volume is proportional to $N$ and a size measure scales as $N^{1/3}$. The proportionality between physical volume and the cube of a radius of gyration depends on shape and density profile. Compactness alone supplies scaling, not a uniquely determined numerical monomer volume.

A poor solvent favors effective attraction between polymer segments relative to solvent contacts. A dilute flexible chain tends to contract, and sufficiently unfavorable conditions produce a compact polymer globule. Solvent quality depends on the polymer, solvent and temperature. The simple Flory–Huggins solution theory identifies the poor-solvent side of the theta condition with $\chi >1/2$; this does not guarantee that every finite-density mixture is inside its spinodal.